Teroson MS 9380 - 290 ml gray sealant

Product detailed description

TEROSON® MS 9380 is an elastomeric industrial adhesive with high tensile strength and rapid skin formation. The product also offers high initial strength and GL (Germanischer Lloyd) approval. It is thixotropic for good bead stability and provides a Shore A hardness of 70 after curing. TEROSON MS 9380 has the following properties:

• Technology Silane Adhesive
• Ingredients Single-component
• Moisture Curing
• Application Assembly of parts
• Appearance White, Grey, Black
_x0 Thixotropic

TEROSON MS 9380 is a one-component, high viscosity, non-sag adhesive based on a silane-modified polymer that cures under the influence of moisture to a permanently flexible material. The skin formation time and curing time depend on humidity and temperature. The final cure also depends on the layer thickness. At elevated temperatures and humidity the curing time is shortened, while at low temperatures and low humidity the curing process is slowed down. g/cm³: approx. 1.45

Non-sag: non-sag (DIN profile 15 mm)

Skin formation time, min*: approx. 4 to 10

Curing speed 3

Shore-A hardness (ISO 868, Durometer A): approx. 70

Tensile strength (according to ISO 37), MPa: approx. 4.0

Elongation at break 120

Strength at 100% elongation (according to ISO 37), MPa: approx. 3.2

Volume change (according to DIN 52451), %: <2

Strength 2.0

Application temperature, °C: 5 to 40 within the working range temperatures, °C: -40 to +100 Short-term (up to 1 hour), °C: 120

_x00 9380 is free of solvents, isocyanates, silicone and PVC. It has very good adhesion to many different materials. This product also shows good resistance to UV radiation and can therefore be used in both interior and exterior applications. TEROSON MS 9380 allows for accelerated curing as a two-component material. 9190 500 ml package or 150 ml package TEROSON MS 9380 is used in the following applications: fillings, panels, roof sheets in the production of vehicles and caravans. Flexible internal and external sealing of joints and seams in the following areas: car bodies, caravans, railway wagons, containers and general metal structures, in the electrical industry, in the production of air conditioning and ventilation systems contaminated with uncured TEROSON MS 9380, we recommend using Teroson FL+.