Loctite EA 9455 - 50 ml two-component epoxy liquid clear

Package sizes:

supplied in 50 ml and 200 ml package.

This product: aluminum

• Potency of the mixed mixture: 3 min
• Handling strength in - 15 min
• For impact loads, and for use in optics
• For bonding steel and stainless steel, aluminum, copper, ,>

  Physical properties:

  • Temperature resistance: -55°C to 80°C
  • Tensile strength: 1.3 N/mm2
  • Shear strength: 16 N/mm2
  Resistance to bed
  • Shore hardness: 80
  • Elongation: 80%
  • Viscosity 3.2 Pa.s - product is liquid

  Very good for bonding aluminum

• Low carbon steel - 14 N/mm2
• Aluminum: 6 - 13 N/mm2
• Stainless steel - 9 N/mm2
• Polycarbonate - 2 N/mm2
• Nylon - 0.3 N/li N/mm2
• ABS - 2 N/mm2
• PVC - 2 N/mm2
• Fiberglass - 3 N/mm2

Loctite EA 9455 has the following properties:

• Technology: liquid
• Viscosity: Low
• Two components - resin and hardener
• Mixing ratio by volume: resin: hardener 1: 1
• Mixing ratio by weight: resin: hardener 100: 105
• Application: Bonding
• Strength: High

Instructions for use:

• For best bonding results, the surfaces to be bonded should be clean, dry and degreased.
• It is necessary to cure before use. Loctite 9455 can be applied directly from the twin cartridges via the supplied static mixer. In this case, squeeze the first 3 to 5 cm into the waste. When using a larger product package, mix both components thoroughly in the exact ratio by volume or weight. When mixing by hand, weigh or measure the required amount of resin and hardener and mix them vigorously until you get a uniform product color. as quickly as possible to one of the surfaces to be bonded. To obtain maximum bond strength, spread the product evenly over both surfaces. The parts should be bonded immediately after application of the mixed adhesive.
• For information on pot life, see section - Typical properties of uncured material. Higher temperatures and smaller amounts of product applied will shorten the pot life.
• Prevent possible movement of the assembled parts during the product curing process. The bonded joint should be left undisturbed until it has gained full strength before the parts are put into service.

  Loctite 9455 (also known as clear liquid epoxy.

  
  
  LOCTITE® EA 9455
  A 2-part, clear, colorless, fast-curing, low-viscosity, high-strength, industrial liquid tough epoxy adhesive.
  LOCTITE® EA 945 is a low-viscosity, high-strength, mercaptan-based industrial liquid tough epoxy adhesive. It is ideal for bonding and potting optical parts such as sensors and lenses. It cures at room temperature once mixed. Key substrates include plastics, metals, glass, wood, ceramics and rubber.